HPMC can be divided into instant type and hot-dissolution type. Instant type products disperse quickly when they encounter cold water and disappear into the water. At this time, the liquid has no viscosity because HPMC is only dispersed in water without real dissolution. About 2 minutes, the viscosity of the liquid gradually increases, forming a transparent viscous colloid. Hot-melt products, when met with cold water, can disperse quickly in hot water and disappear in hot water. When the temperature drops to a certain temperature, the viscosity will slowly appear until it forms a transparent viscous colloid. The hot-melt type can only be used in putty powder and mortar. In liquid glue and paint, there will be grouping phenomenon and cannot be used. The instant type has a wider range of applications. It can be used in putty powder and mortar, as well as liquid glue and paint, without any contraindications.
Hot water dissolution method: Since HPMC does not dissolve in hot water, HPMC can be evenly dispersed in hot water at the initial stage, and then quickly dissolves when cooled. Two typical methods are described as follows:
1) Put the required amount of hot water into the container and heat it to about 70°C. The hydroxypropyl methylcellulose was gradually added under slow stirring, initially the HPMC floated on the surface of the water, and then gradually formed a slurry, which was cooled under stirring.
2), add 1/3 or 2/3 of the required amount of water into the container, and heat it to 70°C, disperse HPMC according to the method of 1), and prepare hot water slurry; then add the remaining amount of cold water to hot water slurry, the mixture was cooled after stirring.
Powder mixing method: mix HPMC powder with a large amount of other powdery substances, mix thoroughly with a mixer, and then add water to dissolve, then HPMC can be dissolved at this time without agglomeration, because there is only a little HPMC in every tiny corner Powder, will dissolve immediately when in contact with water. ——Putty powder and mortar manufacturers are using this method. [Hydroxypropyl methylcellulose (HPMC) is used as a thickener and water retention agent in putty powder mortar. ]